Growth of 1.3-um InGaAsN laser material on GaAs by MBE (CROSBI ID 650636)
Neobjavljeno sudjelovanje sa skupa | neobjavljeni prilog sa skupa
Podaci o odgovornosti
Mars, D. E. , Reed, D. , Kanemura, M. ; Kaneko, Y. , Babić, D.
engleski
Growth of 1.3-um InGaAsN laser material on GaAs by MBE
We have grown bulk GaAsN and InGaAsN quantum well laser structures using molecular beam epitaxy and an electron cyclotron resonance plasma source with N2 gas. X-ray diffraction measurements in GaAsN grown on GaAs were used to determine the concentration of N in the range of 0% to ∼2%. Room temperature photoluminescence (PL) measurements were done on quantum well test structures and half lasers. The PL intensity decreases and the PL full width at half maximum (FWHM) increases as the wavelength increases. Rapid thermal annealing (RTA) at 850 °C for 10 s improves the PL intensity by a factor of 8 and increases the PL peak emission energy by 80 meV. The longest wavelength measured to date in laser structures with single quantum wells of InGaAsN is 1480 nm with a FWHM of 60 meV. Samples with and without RTA were fabricated into broad-area lasers with dimensions of 50×500 μm2.50×500 μm2. Laser devices with RTA operated in the pulsed mode at 1.3 μm with a threshold current density of 9.5 kA/cm2.
Molecular beam epitaxy ; Quantum measurement theory ; Epitaxy ; Temperature measurement ; Quantum wells
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
nije evidentirano
nije evidentirano
Podaci o skupu
HP Conference on Optoelectronic and RF Technology (CORT)
poster
01.01.1998-01.01.1998
Santa Clara (CA), Sjedinjene Američke Države