Investigation of the tribological characteristics of the stainless steel X20Cr13 (CROSBI ID 242428)

Prilog u časopisu | izvorni znanstveni rad

Marušić, Vlatko ; Opačak, Ivan ; Nedić, Bogdan ; Jovanović, Desimir ; Rozing, Goran Investigation of the tribological characteristics of the stainless steel X20Cr13 // Innovations in Discrete Productions, 4 (2016), 2; 39-41

Podaci o odgovornosti

Marušić, Vlatko ; Opačak, Ivan ; Nedić, Bogdan ; Jovanović, Desimir ; Rozing, Goran

engleski

Investigation of the tribological characteristics of the stainless steel X20Cr13

For the purposes of testing tribological characteristics of the stainless steel X20Cr13 designed for the parts of process industry plants for the production of sunflower oil, test samples were made and heat treatment by improving on different hardnesses was performed. Final machine processing of the samples was performed out by grinding and polishing. This way, the different characteristics of the surface layer and the different surface topography were achieved. The paper presents the results of the impact of the hardness on characteristics of the stainless steel X20Cr13. By examining the resistance to the adhesion wear it was concluded that the higher wear was on the test samples which have been in the raw condition and who were also loaded by higher forces. Therefore, the quality of the surface wear greatly affects the surface roughness and the coefficient of friction.

steel X20Cr13 ; tribology ; adhesion wear ; topography ; coefficient of friction

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

Podaci o izdanju

4 (2)

2016.

39-41

objavljeno

1314-8907

Povezanost rada

Strojarstvo