Determination of plasticity of steel N-80 by torsion test and its important for practice (CROSBI ID 679283)
Prilog sa skupa u zborniku | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Mamuzić, Ilija ; Balenović, M. ; Golja, Marijan
engleski
Determination of plasticity of steel N-80 by torsion test and its important for practice
By testing plasticity of the steel N-80 ( Č.8380), which is used for the production of special seamless tubes, on torsion plastometr TC-01 ADAMEL LHOMBARGI high plasticity was found in the temperature range 900-1200°C. Two melts with maximum and minimun carbon content were tested and it was found out that plasticity increases with the production level, the lowest is on cast block, and the highest is on tube blank with the production level 1, 5. At the same time these results were compared with the plasticity test results of the third melt N-80, which had been rejected during the production of seamless tubes. Far lower plasticity was established ( the number of twists to failure on the plastometer nL was 4-5 times smaller that with the two previou melta ). The cause of low plasticity was established by detailed metallographic analysis.
steel N-80 ; seamles tubes ; plasticity ; torsion test ; metallorgraphic analysis
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
115-128.
1984.
objavljeno
Podaci o matičnoj publikaciji
Zbornik radova sa 4. Međunarodnog simpozija o plastičnosti i otporu deformacije
Blečić, Svetozar ; Mišković, Nada
Podgorica : Nikšić: Metalurški fakultet Titograd, Željezara “Boris Kidrić“ Nikšić, Kombinat aluminija Titograd
Podaci o skupu
4. međunarodni simpozij o plastičnosti i otporu deformacije
predavanje
26.06.1984-28.06.1984
Herceg Novi, Jugoslavija