Influence of Chemical Composition on Al-2.5Mg-0.7Li Alloy Microstructural Constituents Development (CROSBI ID 687907)
Prilog sa skupa u zborniku | prošireni sažetak izlaganja sa skupa | međunarodna recenzija
Podaci o odgovornosti
Kozina, Franjo ; Zovko Brodarac, Zdenka ; Petrič, Mitja
hrvatski
Influence of Chemical Composition on Al-2.5Mg-0.7Li Alloy Microstructural Constituents Development
Since the application of aluminum (Al) alloys was expanded to lightweight materials with demands for high strength and stiffness to weight ratio, lithium (Li) and magnesium (Mg) were recognised as a principle (major influencing) alloying elements. Interaction of Li and Mg additions influences on microstructural constituents’ development during solidification. Consequently, the mechanical properties of Al-Mg- Li alloys are revealed as a result of developed microstructural constituents due to element interaction, present thermodynamic parameters and therefore solidification sequence.
Al-Mg-Li alloy, magnesium, lithium, solidification sequence, non-equilibrium conditions, microstructural constituents
nije evidentirano
engleski
Influence of Chemical Composition on Al-2.5Mg-0.7Li Alloy Microstructural Constituents Development
nije evidentirano
Al-Mg-Li alloy, magnesium, lithium, solidification sequence, non-equilibrium conditions, microstructural constituents
nije evidentirano
Podaci o prilogu
34-34.
2018.
objavljeno
Podaci o matičnoj publikaciji
Parunov, Joško ; Kožuh, Stjepan ; Bauer, Branko ; Duić, Neven ; Jokić, Andrej ; Landek, Darko ; Lisjak, Dragutin ; Lulić, Zoran ; Majetić, Dubravko ; Matijević, Božidar ; Runje, Biserka ; Sorić, Jurica ; Terze, Zdravko
Zagreb: Fakultet strojarstva i brodogradnje Sveučilišta u Zagrebu ; Metalurški fakultet Sveučilišta u Zagrebu
978-953-7738-62-4
Podaci o skupu
4th Annual PhD Workshop
predavanje
02.07.2018-02.07.2018
Zagreb, Hrvatska