Testing and mutual comparison of abrasive resistance of directly and indirectly quenched cemented surface layers (CROSBI ID 489978)
Prilog sa skupa u zborniku | sažetak izlaganja sa skupa | međunarodna recenzija
Podaci o odgovornosti
Marušić, Vlatko ; Krumes, Dragomir ; Heffer, Goran
engleski
Testing and mutual comparison of abrasive resistance of directly and indirectly quenched cemented surface layers
The paper compares directly quenched, cemented layers with indirectly quenched layers after carbonization of Č4320 in gaseous atmosphere. The analysis of the surface hardness (HRC) and the heat tretment history (HV1) has shown there are no essential differences between analyzed layers. Testing of abrasive wear resistance of surfaces in contact with SiO2 was carried out on samples under laboratory conditions on Taber-abraser machine, and in practice on components of sunflower oil extracting screw presses. It has been established that in high-pressure conditions, directly quenched layers displayed up to 25% lower abrasive wear resistance between protective layer and the abrasive, when compared with indirectly quenched layers after carbonization. The metalographic analysis of structure showed presence of carbide Cr in the protective layer of directly quenched samples, which is most probably the reason for their high abrasive wear resistance.
wear resistance; abrasion; cemented layers; quenched
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
IV-053-IV-059-x.
2002.
objavljeno
Podaci o matičnoj publikaciji
CIM 2002 Computer Integrated Manufacturing and High Speed Machining
Cebalo, Roko ; Herbert, Schulz
Zagreb: Hrvatska udruga proizvodnog strojarstva (HUPS)
Podaci o skupu
8th International Scientific Conference on Production Engineering - CIM 2002
predavanje
13.06.2002-14.06.2002
Brijuni, Hrvatska