Mechanical Properties of Steel Sheets S 700MC in Conditions of Dynamic Loading and their Modification Possibilities with Temperature annealing (CROSBI ID 498955)

Prilog sa skupa u zborniku | sažetak izlaganja sa skupa | međunarodna recenzija

Mamuzić, I. ; Buršak, M. ; Hidveghy, J. Mechanical Properties of Steel Sheets S 700MC in Conditions of Dynamic Loading and their Modification Possibilities with Temperature annealing // Materials and Metallurgy, Summaries of Lectures / Mamuzić, Ilija (ur.). Zagreb: Hrvatsko metalurško društvo, 2004. str. 211-x

Podaci o odgovornosti

Mamuzić, I. ; Buršak, M. ; Hidveghy, J.

engleski

Mechanical Properties of Steel Sheets S 700MC in Conditions of Dynamic Loading and their Modification Possibilities with Temperature annealing

Article deals with the mechanical, fatigue and brittle fracture properties of steel sheets of mark S 700 MC with minimum yield stress of 700 MPa. The chemical composition and technogical regime of rolling process were changed during development of studies steel. The experimental programme was realized at 7 randomly selected meltages (26 coiled sheets) of hot rolled steel sheets with the thickness of 8 and 10 mm. Tensile test showed that 14% of steel sheets had the lower yield stress level like was prescribed (Rm about 21 %) whereas the lower values were measured in longitudinal direction (Re about 9, 9%). Deformation properties in the rolling direction were higher about 38%. The scatter of mechanical properties is not affected by the thickness of steel sheets. The anisotropy of mechanical properties given by the ratio ReL / ReT is in the range from 0, 91 up to 1, 05, RmL / RmT in the range 0, 93 to 0, 97 and A5L / A5T from 1, 0 to 1, 38. Brittle fracture properties of studied steel is guaranteed at 0 °C by notch toughness KCU = 60 J• cm– 2. When U-notch was used, all studied steel sheets successfully passed notch toughness test al – 20 °C for guaranteed level 35 J• cm– 2.

mechanical properties; steel sheets

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

Podaci o prilogu

211-x.

2004.

objavljeno

Podaci o matičnoj publikaciji

Materials and Metallurgy, Summaries of Lectures

Mamuzić, Ilija

Zagreb: Hrvatsko metalurško društvo

Podaci o skupu

6. Međunarodni simpozij Hrvatskog metalurškog društva, SHMD 2004 : materijali i metalurgija

poster

20.06.2004-24.06.2004

Šibenik, Hrvatska

Povezanost rada

Metalurgija