Preparation and Characterization of Transparent gamma-AlOOH Film (CROSBI ID 112633)
Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Musić, Svetozar ; Dragčević, Đurđica ; Popović, Stanko ; Turković, Aleksandra
engleski
Preparation and Characterization of Transparent gamma-AlOOH Film
Experimental conditions for the preparation of transparent gamma-AlOOH (boemite) films were investigated. Transmission electron microscopy revealed a fibrous morphology of gamma-AlOOH particles. Transparency of the films for visible light was preserved up to 900 oC, while after heating up to 1050 oC the film became white. X-ray powder diffraction showed the transition from gamma-AlOOH (90oC) to gamma-Al2O3 (500 to 900oC)and finnaly to alpha-Al2O3 and theta-Al2O3 (1050 oC). Electrical conductivity of the film was measured.
TEM ; IS ; XRD ; AlOOH ; film