Effect of chloride concentration range on the corrosion resistance of Cu-xNi alloys

The anodic behaviour of Cu-xNi alloys and Cu and Ni metals was studied in slightly alkaline solutions containing CI- ions in the concentration range from 0.01 to 2.0 mol/dm^3. The morphology and composition of the surface films formed by anodic polarization were analysed by scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). On the basis of quasi-potentiodynamic polarization data, E_c against c(NaCl) diagrams were constructed, where E_c is the critical pitting potential. These diagrams allow the determination of areas where the materials are susceptible to localized pitting attack. A critical chloride concentration exists below which the resistance to localized corrosion increases with decreasing nickel content and above which it increases with increasing nickel content. This effect is connected with the change in the corrosion resistance observed for the pure metal constituents, i.e., copper and nickel as a function of chloride concentration. The kinetic parameters of pitting corrosion of Cu-xNi alloys reflect the specific properties of both elements and suggest that an increase in Ni content above 40 % would not have a significant effect on the corrosion resistance of Cu-xNi alloys.

copper; Cu-xNi alloys; EDS; localized pitting attack; nickel; SEM

nije evidentirano