Influence of Zn-dopant on the precipitation of alpha-FeOOH in highly alkaline media

The influence of Zn-dopant on the precipitation of alpha-FeOOH in highly alkaline media was monitored by X-ray diffraction (XRD), 57Fe Mössbauer and Fourier transform infrared (FT-IR) spectroscopies and field emission scanning electron microscopy (FE SEM). Acicular and monodisperse alpha-FeOOH particles were precipitated at a very high pH by adding a tetramethylammonium hydroxide solution to an aqueous solution of FeCl3. The XRD analysis of the samples precipitated in the presence of Zn2+ ions showed the formation of solid solutions of alpha-(Fe, Zn)OOH up to a concentration ratio r = [Zn]/([Zn]+[Fe]) = 0.0909. ZnFe2O4 was additionally formed in the precipitate for r = 0.1111, whereas the three phases alpha-FeOOH, alpha-Fe2O3 and ZnFe2O4 were formed for r = 0.1304. In the corresponding FT-IR spectra, the Fe-OH and Fe-O stretching bands were sensitive to the Zn2+ substitution, whereas the Fe-OH bending bands of alpha-FeOOH at 892 and 796 cm-1 were almost insensitive. The Mössbauer spectra showed a high sensitivity to the formation of alpha-(Fe, Zn)OOH solid solutions which were monitored on the basis of a decrease in Bhf values in dependence on Zn-doping. A strictly linear decrease in Bhf for alpha-FeOOH doped with Zn2+ ions was measured up to r = 0.0291, whereas for r = 0.0476 and higher there was a deviation from linearity. The presence of alpha-(Fe, Zn)OOH, alpha-Fe2O3 and ZnFe2O4 phases in the samples was determined quantitatively by Mössbauer spectroscopy. Likewise, Mössbauer spectroscopy did not show any formation of the solid solutions of alpha-Fe2O3 with Zn2+ ions. FE SEM showed a strong effect of Zn-doping on the elongation of acicular alpha-FeOOH particles (~ 500-700 nm in length) up to r = 0.1111. For r = 0.1304 the sizes of ZnFe2O4 particles were around 30-50 nm, and those of alpha-Fe2O3 particles were around 500 nm, whereas a relatively small number of very elongated alpha-(Fe, Zn)OOH particles was observed. A possible mechanism of the formation of alpha-(Fe, Zn)OOH, alpha-Fe2O3 and ZnFe2O4 particles was suggested.

Zn-dopant ; Tetramethylammonium hydroxide ; alpha-FeOOH ; alpha-Fe2O3 ; ZnFe2O4 ; XRD ; 57Fe Mössbauer ; FT-IR ; FE SEM ; EDS

nije evidentirano