Hydrogen evolution during cathodic polarisation of Al-Ga alloy
The results presented in this paper were obtained with three Al-Ga binary alloys that had been prepared on super pure (99.999 %) Al base. The yield of hydrogen formed during cathodic polarisation of Al-Ga alloys in a neutral salt solution was measured volumetrically as a function of current density, temperature (between 20 and 80°C) and gallium content in the alloy (0.1, 0.26 and 2.6 wt. % Ga respectively). The yield of hydrogen was established to be about 2 or even less at all current densities and at low temperatures, while with increasing temperature it approached the value of 4. The yield of hydrogen decreases with the increase of gallium content in the alloy especially at lower temperatures.
Al-Ga alloys; cathodic polarisation; hydrogen evolution
Programme and Book of abstract of the 4th Croatian Symposium on Electrochemistry ; ISBN 953-6894-26-2
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
296-299-x.
2006.
objavljeno
Podaci o matičnoj publikaciji
Gojo, Miroslav ; Mandić, Zoran
Primošten: Hrvatsko društvo kemijskih inženjera i tehnologa (HDKI)
953-6894-27-0
Podaci o skupu
4. hrvatski simpozij o elektrokemiji
predavanje
28.05.2006-01.06.2006
Primošten, Hrvatska