Preparation, characterization and luminescence of nanocrystalline Y2O3:Ho (CROSBI ID 132411)

Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija

Biljan, Tomislav ; Gajović, Andreja ; Meić, Zlatko ; Meštrović, Ernest Preparation, characterization and luminescence of nanocrystalline Y2O3:Ho // Journal of alloys and compounds, 431 (2007), 1-2; 217-220. doi: 10.1016/j.jallcom.2006.05.050

Podaci o odgovornosti

Biljan, Tomislav ; Gajović, Andreja ; Meić, Zlatko ; Meštrović, Ernest

engleski

Preparation, characterization and luminescence of nanocrystalline Y2O3:Ho

Nanocrystalline Y2O3:Ho was synthesized by solution combustion method with ethylene glycol as fuel. Material was characterized using powder X-ray diffraction and transmission electron microscopy (TEM). X-ray diffraction and TEM showed that the material is nanostructured. Luminescence properties were studied using Raman spectrometers with excitation in near infrared (NIR) and visible regions. The visible and NIR luminescence spectra of nanocrystalline Y2O3:Ho show some important differences from those of bulk material. The convenience of using Raman instruments for studying luminescence of lanthanide ions is demonstrated.

Y2O3 ; holmium ; luminesence ; X-ray diffraction ; transmisson electron microscopy

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

Podaci o izdanju

431 (1-2)

2007.

217-220

objavljeno

0925-8388

10.1016/j.jallcom.2006.05.050

Povezanost rada

Fizika, Kemija

Poveznice
Indeksiranost