Influence of synthesis procedure on the morphology of bismuth oxide particles (CROSBI ID 132675)
Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Gotić, Marijan ; Popović, Stanko ; Musić, Svetozar
engleski
Influence of synthesis procedure on the morphology of bismuth oxide particles
A modified sol-gel procedure, based on the esterification reaction, was used to prepare the Bi2O3 precursor, which was then heated to 400 or 500 °C. β -Bi2O3 obtained at 400 °C showed well-shaped plate-like particles. The mixture β -Bi2O3/α -Bi2O3, obtained by prolonged heating at 400 °C, yielded pseudospherical particles having about 100 nm in size and much larger particles, as found by FE SEM. α -Bi2O3 obtained at 500 °C consisted of particles of varying shapes and sizes. Vitrification of α -Bi2O3 was also observed. XRD showed a small fraction of unidentified phase(s) in these samples. Different microstructures were obtained when the precipitation from aqueous Bi(NO3)3 solution with tetramethylammonium hydroxide at pH ∼ 14 was used. The precipitation at pH ∼ 3.5 yielded cloverleaf-like particles of good uniformity, which were assigned to BiOOH (isomorphous with (La0.26Bi0.24)Bi0.5OOH. It was found that these particles were made up of much smaller primary BiOOH particles.
sol-gel; bismuth oxide; Bi2O3; XRD; FE SEM
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano