Some properties of composite resins cured by pulsed blue laser (CROSBI ID 85882)
Prilog u časopisu | izvorni znanstveni rad
Podaci o odgovornosti
Tarle, Zrinka ; Meniga, Andrej ; Knežević, Alena ; Šutalo, Jozo ; Pichler, Goran ; Ristić, Mira
engleski
Some properties of composite resins cured by pulsed blue laser
The purpose of the study was to analyse some properties of composite resin samples cured by pulsed laser in comparison with standard halogen light. Three bybrid and three microfilled commercial composite materials were polymerized in the experimental conditions using an excimer laser pumped dye laser (XeCl Lambda Physik LPX 100/LPD 3002) and a standard curing unit (Heliolux GTE). The samples were spectroscopically analysed (FTIR) for the degree of conversion, scanning electron microscopy (SEM) was performed for characterising the structure of the material, and volumetric shrinkage behaviour was tested using density bottle method. Statistical analysis of the data (ANOVA p<0.05) shoes that the degree of conversion values obtained by excimer laser was significantly higher for all the materials and shades tested while the polymerization shrinkage values were significantly lower compared with the conventional curing unit. Those results are clinically very important in situations whenever close approximation of the light curing tip to the composite surface is impossible. The monochromatic pulsed dye laser set at 468 nm allows high penetration into the sample and the nature of the pulse allows homogeneous high quality curing with decreased shrinkage of the composite resin. The sensitivity of the tooth after the placement of direct composite restoration is mainly connected with the polymerization contraction. Adhesive and cohesive fractures appear in dentin, hybrid layer and material itself. The amount of volumetric increase is in accordance with the degree of cure, the type of composite material and the nature of the activating light.
composite materials; photopolymerization
nije evidentirano
hrvatski
Svojstva kompozitnih materijala polimeriziranih pulsnim laserom
Svrha rada bila je raščlaniti pojedina svojstva uzoraka kompozitnih smola polimeriziranih pulsnim laserom u usporedbi sa standardnom žaruljom. Tri hibridna i tri mikropunjena kompozitna materijala polimerizirani su, u eksperimentalnim uvjetima, uporabom excimer i dye lasera (XeCl Lambda Physik LPX 100/LPD 3002) i standardne halo gene žarulje (Heliolux GTE). Uzorci su raščlanjeni spektroskopski (FTIR) za određivanje stupanja konverzije, scanning elektronskim mikroskopom za raščlambu strukture materijala, a ponašanje volume- trijskoga skupljanja testirano je s pomoču piknometra. Statistička raščlamba podataka (ANOVA, p<0,05) pokazala je znatno veće vrijednosti stupnja konverzije dobivene pri polimerizaciji pulsnim laserom za sve ispitivane materijale i boje, a rezultati polimerizacijskoga skupljanja znatno su niži u usporedbi s rezultatima dobivenim standardnom Žaruljom. Ti su rezultati klinički vrlo važni u okolnostima kada je teško postići blizak doticaj uređaja za polimerizaciju i površine kompo- zitnog ispuna. Monokromatski pulsni laser, pri valnoj dužini od 468 nm, omogućuje snažan prodor svjetla u uzorak, a priroda pulsa osigurava homogeno, visokokvalitetno stvrdnjavanje sa smanjenim skupljanjem kompozitne smole. Osjetljivost zuba nakon aplikacije izravnoga kompozitnog ispuna većinom je povezana s polimerizacijskim skupljanjem. Adhezijske i kohezijske frakture događaju se u dentinu, hibridnom sloju i u samome materijalu. Veličina volumetrijskih promjena povezana je sa stupnjem konverzije, vrstom kompozitnoga materijala i prirodom svjetla za polimerizaciju.
kompozitne smole; laser; konverzija monomera; polimerizacijsko skupljanje
nije evidentirano