Formation and characterization of nanosize α -Rh2O3 particles
Amorphous rhodium (hydrous)oxide precursor was prepared from Rh(NO3)3 aqueous solution using NH4OH solution as a precipitating agent. The precipitate was subsequently washed, dried at 60°C, then heated in air atmosphere up to 650°C. Samples were characterised by XRPD, FT-IR, RAMAN, FE-SEM and EDS. The XRPD of sample prepared at 400°C showed a broad and intensive peak, which can be assigned to the amorphous nature of this sample. The peak was positioned at Bragg angles corresponding to the prominent peaks of α -Rh2O3. For the same sample the FT-IR spectrum showed one very broad band centred at 544 cm-1. On the other hand, the Raman spectrum of the same sample showed broad peaks at 268, 411, and 556 cm-1, which can be assigned to poorly crystallized α -Rh2O3. The Raman spectrum of the sample prepared at 650°C showed bands at 276, 422, 568 and 610 cm-1, which can be assigned to α -Rh2O3 particles. The sample prepared at 500°C also contained RhO2 as an intermediate phase. FE-SEM images showed a gradual increase in size of α -Rh2O3 particles (in the nanometer range), prepared from 400 to 650°C.
α -Rh2O3 ; XRPD ; FT-IR ; Raman ; FE-SEM
Rad je prezentiran na XXIX European Congress on Molecular Spectroscopy : Molecular Spectroscopy and Molecular Structure 2008 održanom od 31.08.-05.09.2008., Opatija, Hrvatska.
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o izdanju
924-926
2009.
221-224
objavljeno
0022-2860
10.1016/j.molstruc.2008.10.017