Chemically controlled particulate properties of zeolites : towards the face-less particles of zeolite A. 1. Influence of the batch molar ratio [SiO2/Al2O3]b on the size and shape of zeolite A crystals (CROSBI ID 167626)
Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Kosanović, Cleo ; Antonić Jelić, Tatjana ; Bronić, Josip ; Kralj, Damir ; Subotić, Boris
engleski
Chemically controlled particulate properties of zeolites : towards the face-less particles of zeolite A. 1. Influence of the batch molar ratio [SiO2/Al2O3]b on the size and shape of zeolite A crystals
Influence of the batch molar ratio y = [SiO2/Al2O3]b on the size and shape of zeolite A crystals at three different molar ratios [SiO2/H2O]b and [Na2O/H2O]b was investigated. Four different morphological entities of zeolite A, namely regular cubic crystals with sharp edges and apexes, cubic crystals with truncated edges, cubic crystals with “rounded” edges and apexes and pseudo-spherical, face-less particles, were observed in the crystalline end products obtained by hydrothermal treatment (heating at 80 oC) of the hydrogels having [SiO2/Al2O3]b in the range 1.0 – 2.2, [SiO2/H2O]b in the range 0.006 – 0.0186 and [Na2O/H2O]b in the range 0.0136 - 0.0424. The chemical conditions with respect to the values of [SiO2/Al2O3]b, [SiO2/H2O]b and [Na2O/H2O]b for obtaining the particular morphological entities of zeolite A are defined, and the possible mechanisms of their formation are discussed. The influence of the mentioned factors on the crystal size and the surface properties of crystallized zeolites is also considered.
aluminosilicate hydrogels ; crystallization ; zeolite A ; crystal morphology ; crystal size ; specific surface area
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o izdanju
137 (1/3)
2011.
72-82
objavljeno
1387-1811
1873-3093
10.1016/j.micromeso.2010.08.024