X-ray diffraction and Mössbauer spectroscopy of the system m-ZrO2-alpha-Fe2O3 (CROSBI ID 584060)
Prilog sa skupa u zborniku | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Popović, Stanko ; Gržeta, Biserka ; Štefanić, Goran ; Czako-Nagy, Ilona ; Musić, Svetozar
engleski
X-ray diffraction and Mössbauer spectroscopy of the system m-ZrO2-alpha-Fe2O3
X-ray diffraction showed that the terminal solid solubility limits at room temperature (RT) were: (2.0+/-0.3) mol% of alpha-Fe2O3 in m-ZrO2 and (1.0+/-0.3) mol% of m-ZrO2 in alpha-Fe2O3. The unit-cell parameters of the sample m-Zr0.995Fe0.010O2.005 were found different from those of m-ZrO2, indicating an asymmetric distortion of the crystal lattice of m-ZrO2 caused by dissolution of only 0.5 mole % of alpha-Fe2O3. The 57Fe Moessbauer spectrum (RT) of the same sample showed a quadrupole doublet with parameters d = 0.299 mm s-1 and delta = 1.256 mm s-1, which can be ascribed to the formation of solid solutions at the ZrO2-rich side. Similarly, the decreased value of hyperfine magnetic splitting indicated the formation of solid solutions at the Fe2O3-rich side.
Zirconia. m-ZrO2-alpha-Fe2O3 system. Structural properties.
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
193-196.
1996.
objavljeno
Podaci o matičnoj publikaciji
ICAME-95
I. Ortalli
Bolonja: Societa Italiana di Fisica, Editrice Compositori
Podaci o skupu
Nepoznat skup
poster
29.02.1904-29.02.2096