Vacuum brazing of aluminium metal matrix composite (55 vol.% SiCp/A356) using aluminium-based filler alloy (CROSBI ID 182195)

Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija

Niu, Jitai ; Luo, Xiangwei ; Tian, Hao ; Brnić, Josip Vacuum brazing of aluminium metal matrix composite (55 vol.% SiCp/A356) using aluminium-based filler alloy // Materials science & engineering. B, Solid-state materials for advanced technology, 177 (2012), 19; 1707-1711. doi: 10.1016/j.mseb.2011.12.042

Podaci o odgovornosti

Niu, Jitai ; Luo, Xiangwei ; Tian, Hao ; Brnić, Josip

engleski

Vacuum brazing of aluminium metal matrix composite (55 vol.% SiCp/A356) using aluminium-based filler alloy

Aluminium matrix composites with high volume fractions of SiC particles, as the reinforcements, are potentially suitable materials for electronic packaging. These composites, due to their poor weldability, however, have very limited applications. The microstructure and shear strengths of the bonds made in 55 vol.% SiCp/A356 composite, using an aluminium based filler alloy containing Cu, Si, Mg and Ni, were investigated in this paper. The brazing temperature had a clear effect on the bond integrity, and the samples brazed at 560 °C demonstrated good bonding between the filler alloy and the SiC particles. The maximum shear strength achieved in this work was 102 MPa.

aluminium matrix composites ; vacuum brazing ; microstructure ; shear strength

S.I.: Structural Materials : Properties, Microstructure and Processing ; Zhou Guangtao i Jitai Niu (ur.).

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

Podaci o izdanju

177 (19)

2012.

1707-1711

objavljeno

0921-5107

10.1016/j.mseb.2011.12.042

Povezanost rada

Brodogradnja, Strojarstvo, Temeljne tehničke znanosti

Poveznice
Indeksiranost