The overaging kinetics of Al–Zn–Mg–Cu alloy (CROSBI ID 587883)
Prilog sa skupa u časopisu | sažetak izlaganja sa skupa | međunarodna recenzija
Podaci o odgovornosti
Chushkov, A. P. ; Šipalo Žuljević, J.
engleski
The overaging kinetics of Al–Zn–Mg–Cu alloy
The overaging kinetics of Al–Zn–Mg–Cu alloy at 440–460 K was investigated by electrical resistivity and tensile property measurements, which were supplemented by TEM and differential scanning calorimetry (DSC). Overaging in this alloy system was shown to follow classical coarsening behaviour as characterised by a time<sup>-1/3</sup> particle size dependence. Precipitate dissolution under non-isothermal conditions (DSC) had an activation energy (~135 kJ mol<sup>-1</sup>) closer to that for diffusion.
Al–Zn–Mg–Cu alloy
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
392-392.
2012.
nije evidentirano
objavljeno
Podaci o matičnoj publikaciji
Podaci o skupu
10<sup>th</sup> international symposium of Croatian Metallurgical Society SHMD '2012 : Materials and Metallurgy
poster
17.06.2012-21.06.2012
Šibenik, Hrvatska