Degradation of microstructure in plain and platinum aluminide coatings on superalloy ZhS6U during isothermal oxidation (CROSBI ID 587884)
Prilog sa skupa u časopisu | sažetak izlaganja sa skupa
Podaci o odgovornosti
Kuroles, L. M. ; Pyontkovsky, F. K. ; Živković, V.
engleski
Degradation of microstructure in plain and platinum aluminide coatings on superalloy ZhS6U during isothermal oxidation
Isothermal oxidation at 1100°C of a high activity plain aluminide coating and a platinum aluminide coating, developed by the pack cementation technique, on cast nickel base superalloy ZhS6U has been carried out with the primary objective of systematically understanding the coating degradation process during oxidation. The microstructural degradation of both the plain aluminide and platinum aluminide coatings during oxidation was seen to occur in three distinct stages which, however, differed for each coating. This stagewise degradation, which involves final obliteration of the interdiffusion layer in each case, is discussed in detail.
superalloy ZhS6U ; isothermal oxidation
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
392-392.
2012.
nije evidentirano
objavljeno
Podaci o matičnoj publikaciji
Podaci o skupu
10th international symposium of Croatian Metallurgical Society SHMD '2012 : Materials and Metallurgy
poster
17.06.2012-21.06.2012
Šibenik, Hrvatska