Failure of ultra high strength low alloy steel (CROSBI ID 587902)
Prilog sa skupa u časopisu | sažetak izlaganja sa skupa | međunarodna recenzija
Podaci o odgovornosti
Mitrofanov, H. L. ; Jakšić, D.
engleski
Failure of ultra high strength low alloy steel
An ultra high strength low alloy steel having the composition Fe-0, 25C-1, 4Cr-0, 8Mo-0, 3V-0, 1Nb (wt.%), has been developed using the electroslag refining process. In order to understand the failure behaviour of the material, tensile coupons, surface crack tension specimens, compact tension specimens, and pressure chambers were fabricated and tested. To select a suitable failure theory for this material, failure assessment has been carried out on pressure chambers and verified with test results. Fracture analysis has also been carried out on the cylindrical vessels containing axial surface cracks and it was found that failure pressure decreases with increasing in crack size.
low alloy steel
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
396-396.
2012.
nije evidentirano
objavljeno
Podaci o matičnoj publikaciji
Podaci o skupu
10<sup>th</sup> international simposium of Croatian Metallurgical Society SHMD '2012 : Materials and Metallurgy
poster
17.06.2012-21.06.2012
Šibenik, Hrvatska