Influence of temperature on bulk-fill composites’ post-cure degree of conversion (CROSBI ID 616686)

Prilog sa skupa u časopisu | sažetak izlaganja sa skupa | međunarodna recenzija

Par, Matej ; Gamulin, Ozren ; Marović, Danijela ; Klarić, Eva ; Negovetić Mandić, Višnja ; Tarle, Zrinka Influence of temperature on bulk-fill composites’ post-cure degree of conversion // Journal of dental research. 2014. str. 118-118

Podaci o odgovornosti

Par, Matej ; Gamulin, Ozren ; Marović, Danijela ; Klarić, Eva ; Negovetić Mandić, Višnja ; Tarle, Zrinka

engleski

Influence of temperature on bulk-fill composites’ post-cure degree of conversion

Objective: To investigate the effect of temperature on the post-cure behavior of one conventional and three bulk-fill composite materials. Methods: A conventional composite GrandioSO (GR) and three bulk-fill composites: Tetric EvoCeram Bulk Fill (TECBF), Quixfil (QF) and X- tra fil (XF) were investigated. The samples were cured for 20 seconds with irradiance of 1090 mW/cm2. For each composite, 10 samples were prepared and randomly divided into two groups: the “room-temperature group” (RTG, n=5) and the “body- temperature group” (BTG, n=5) which were stored in dark at 20°C and 37°C, respectively. Degree of conversion (DC) was determined by means of Raman spectroscopy. DC measurements were made at the sample surface immediately after curing (0h) and 24h post-cure (24h). To analyze the extent of post-cure DC increase, 0h-RTG/24h-RTG and 0h- BTG/24h-BTG were compared for each composite by dependent samples t-test. To analyze the difference in DC between RTG and BTG, the DC values of 0h- RTG/0h-BTG and 24h-RTG/24h-BTG were compared for each composite by independent samples t- test. Results: DC values (%) (0h/24h) for RTG were: GR 60.5/68.6, TECBF 59.3/65.6, QF 64.4/72.6, XF 63.6/71.5 ; for BTG: GR 58.0/73.8, TECBF 61.6/76.7, QF 65.8/78.3, XF 60.9/75.0. DC increase 24h post-cure was significant for all composites and ranged between 6.3%-8.2% in RTG and 12.5%-15.7% in BTG. Since there was no significant difference between 0h-RTG and 0h- BTG for each individual composite, equal initial DC for both groups was assumed. The impact of temperature on post-cure behavior was evaluated by comparing 24h- RTG/24h-BTG. All composites demonstrated higher DC in 24h-BTG compared to 24h-RTG. The difference was statistically significant for GR, TECBF and QF, while for XF only a trend of increase was observed. Conclusion: Post-cure temperature increase from 20°C-37°C yielded higher post-cure DC increase, which should be taken into account while investigating composite properties. This study was supported by Croatian Science Foundation.

composites ; dental materials ; polymerization

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

Podaci o prilogu

118-118.

2014.

nije evidentirano

objavljeno

Podaci o matičnoj publikaciji

Journal of dental research

0022-0345

1544-0591

Podaci o skupu

International Association for Dental Research Pan- European Region Congress 2014

poster

10.09.2014-13.09.2014

Dubrovnik, Hrvatska

Povezanost rada

Dentalna medicina, Fizika

Indeksiranost