Elements Diffusion in Brazing Seam of High Volume Fraction SiCp/6063Al Matrix Composites (CROSBI ID 626377)
Prilog sa skupa u zborniku | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
CHENG, Dongfeng ; NIU, Jitai ; GAO, Zeng ; Brnić, Josip
engleski
Elements Diffusion in Brazing Seam of High Volume Fraction SiCp/6063Al Matrix Composites
In this research, 6063 aluminum matrix composites containing 55-75% SiC particle reinforcing phase was selected as the parent metal and Al-Cu24-Si5-Zn2-Ti1 alloy metal was selected as the filler metal. After nickel plating of the parent metal, the brazing process is carried out on vacuum brazing furnace under the temperature of 565℃, 570℃ and 575℃ and holding for 10 minutes, 20 minutes and 30 minutes. The interfacial microstructure is investigated by light optical microscopy (LOM), scanning electron microscopy (SEM), and the element diffusion is analyzed by energy spectrum analysis (EDS). The result shows that the nickel plating layer on the surface of parent metal not only metalizes the SiC particle, but also participates in the diffusion process. The element distribution in the brazing seam is described exactly. Finally, the reason why finest crystalline grains and evenest distribution could be achieved under brazing temperature of 575℃ and holding for 30 minutes is analyzed.
Vacuum Brazing; Seam; Filler Metal; Elements Diffusion
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
2015.
objavljeno
Podaci o matičnoj publikaciji
Podaci o skupu
Frontiers in Materials Processing, Application, Research and Technology (FiMPART 15)
predavanje
12.06.2015-15.06.2015
Hyderābād, Indija