Effect of electrolyte temperature on the thickness of anodic aluminum oxide (AAO) layer (CROSBI ID 225740)

Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija

Michal, P. ; Vagaska, A. ; Fechova, E. ; Gombar M. ; Kozak, Drazan Effect of electrolyte temperature on the thickness of anodic aluminum oxide (AAO) layer // Metalurgija, 55 (2016), 3; 403-406

Podaci o odgovornosti

Michal, P. ; Vagaska, A. ; Fechova, E. ; Gombar M. ; Kozak, Drazan

engleski

Effect of electrolyte temperature on the thickness of anodic aluminum oxide (AAO) layer

Effect of electrolyte temperature on the thickness of resulting oxide layer has been studied. Unlike previous published studies this article was aimed to monitor the relationship between electrolyte temperature and resulting AAO layer thickness in interaction with other input factors affecting during anodizing process under special process condition, i.e. lower concentration of sulphuric acid, oxalic acid, boric acid and sodium chloride. According to Design of Experiments (DOE) 80 individual test runs of experiment were carried out. Using statistical analysis and artificial intelligence for evaluation, the computational model predicting the thickness of oxide layer in the range from 5 / µm to 15 / µm with tolerance ± 0, 5 / µm was developed.

Anodic Aluminium Oxide (AAO) ; layer thickness ; electrolyte ; temperature ; oxidation

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

Podaci o izdanju

55 (3)

2016.

403-406

objavljeno

0543-5846

1334-2576

Povezanost rada

Strojarstvo

Poveznice
Indeksiranost