The Effect of Tempering on Mechanical Properties of Cold-Rolled 42CrMo4 Steel Pipes (CROSBI ID 94334)
Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Gojić, Mirko
engleski
The Effect of Tempering on Mechanical Properties of Cold-Rolled 42CrMo4 Steel Pipes
The effect of tempering on mechanical properties of cold rolled 42CrMo4 steel pipes was studied. The production of pipes consisted of the hot rolled+annealing at 700oC+cold rolling+quenching with subsequent tempering. By annealing of seamles pipes at 700oC under industrial conditions and using protective atmosphere and cold rolling, the tempering bainite microstructure was observed. Quenching and tempering of pipes in laboratory conditions resulted in a high yield strength (986-1230 MPa), combined with a high impact toughness value at 20oC (46.1-66.9 J/cm2). the strength of pipes shows a continuous decrease with the increase in tempering parameter. Decrease in strength is due to the spheroidization of carbides and the recovery of the microstructure. the most important observation is that it is possible to use this technique for the production of pipes in order to optimize the strength and toughness of 42CrMo4 steel pipes.
steel; cold-rolling; pipes; tempering; mechanical properties; microstructure
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano