Correlation of the precursor type with densification behavior and microstructure of sintered mullite ceramics (CROSBI ID 94871)

Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija

Ivanković, Hrvoje ; Tkalčec, Emilija ; Nass, Ruediger ; Schmidt, Helmut Correlation of the precursor type with densification behavior and microstructure of sintered mullite ceramics // Journal of the European Ceramic Society, 23 (2003), 283-292-x

Podaci o odgovornosti

Ivanković, Hrvoje ; Tkalčec, Emilija ; Nass, Ruediger ; Schmidt, Helmut

engleski

Correlation of the precursor type with densification behavior and microstructure of sintered mullite ceramics

The effect of alumina component in diphasic mullite precursors containing alkoxy-derived silica on the crystallization and sintering behavior of compacts was studied. The phenomena observed were characterized using differential thermal analysis (DTA), powder X-ray diffraction (XRD), dilatometry and transmission and scanning electron microscopy (TEM, SEM). In order to change the characteristics of as-prepared gels, the alumina source was varied while keeping the silica source constant. Al(NO3)3.9H2O, gamma-Al2O3 and boehmite (gamma-AlOOH) were used as the alumina source and TEOS as the silica source. Clear differences were found in the microstructure of sinterd samples derived from the precursors with aluminum nitrate nonahydrate in comparison to the samples containing gamma-Al2O3 or boehmite (gamma-AlOOH). The former exhibited elongated mullite grains embedded into the "equiaxial mullite matrix". This morphology is due to the overlapping of mullite crystallization and viscous flow sintering temperatures. Transient alumina, either added as gamma-Al2O3 or formed in situ by decomposition of boehmite, shifts the mullite formation above the sintering temperature, and enables formation of equiaxial mullite. The smaller are the transient alumina particles, the smaller are mullite grains of sintered bodies.

Grain size; Microstructure; Mullite; Sintering; Sol-gel processes

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

Podaci o izdanju

23

2003.

283-292-x

objavljeno

0955-2219

Povezanost rada

Fizika, Kemijsko inženjerstvo

Indeksiranost