Phase transformation and microstructure study of the as-cast Cu-rich Cu-Al-Mn ternary alloys (CROSBI ID 242719)
Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Holjevac Grgurić, Tamara ; Manasijević, Dragan ; Kožuh, Stjepan ; Ivanić, Ivana ; Balanović, Ljubiša ; Anžel, Ivan ; Kosec, Borut ; Bizjak , Milan ; Knežević, Monika ; Gojić, Mirko
engleski
Phase transformation and microstructure study of the as-cast Cu-rich Cu-Al-Mn ternary alloys
Four Cu-rich alloys from the ternary Cu-Al-Mn system were prepared in the electric-arc furnace and casted in cylindrical moulds with dimensions: =8 mm and length 12 mm. Microstructural investigations of the prepared samples were performed by using optical microscopy (OM) and scanning electron microscopy, equipped by energy dispersive spectroscopy (SEM-EDS). Assignation of crystalline phases was confirmed by XRD analysis. Phase transition temperatures were determined using simultaneous thermal analyzer STA DSC/TG. Phase equilibria calculation of the ternary Cu-Al- Mn system was performed using optimized thermodynamic parameters from literature. Microstructure and phase transitions of the prepared as-cast alloys were investigated and experimental results were compared with the results of thermodynamic calculations.
Cu-Al-Mn alloys, SMA alloys, microstructure, phase transformations
Glavni autor: Tamara Holjevac Grgurić
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o izdanju
53 (3)
2017.
413-422
objavljeno
1450-5339
2217-7175
10.2298/JMMB170809039H
Povezanost rada
Kemijsko inženjerstvo, Metalurgija