Push-out bond strength of three different calcium silicate-based root-end filling materials after ultrasonic retrograde cavity preparation (CROSBI ID 243757)
Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Kadić, Snježana ; Baraba, Anja ; Miletić, Ivana ; Ionescu, Andrei ; Brambilla, Eugenio ; Malčić Ivanišević, Ana ; Gabrić, Dragana
engleski
Push-out bond strength of three different calcium silicate-based root-end filling materials after ultrasonic retrograde cavity preparation
Objective The aim of this study was to evaluate the bond strength of three calcium silicate- based root-end filling materials. Materials and methods The root canals of 30 single-rooted teeth were endodontically treated ; their root ends were resected and root-end cavities were prepared using ultrasonic tip.Theteethwererandomlydividedintothreegroupsa ccordingtothematerial:(1)Micro- Megamineraltrioxideaggregate (MM- MTA), (2) Biodentine, and (3) TotalFill root repair material (RRM). Push-out test was performed using universal testing machine, and failure mode was analyzed by stereomicroscope. The data were statistically analyzed using KruskalWallis and Man-Whitney post hoc tests. All p values <0.05 were considered significant. Results TotalFill RRM exhibited significantly higher bond strength (12.69 MPa) than Biodentine (9.34 MPa, p = 0.023) andMM- MTA(7.89MPa, p=0.002).Thedifferencebetween Biodentine and MM-MTA was not significant (p = 0.447). Mixed failures were the most noted in all three groups. MMMTA had more adhesive failures than Biodentine and TotalFill, and no cohesive failures, but without statistical significance (p = 0.591). Conclusion The bond strength was the highest for TotalFill RRM. Clinical relevance In order to provide a persistent apical seal, root- end filling materials should resist dislodgement under static conditions, during function and operative procedures. TotalFill RRM exhibited higher bond strength to dentin than MM-MTA and Biodentine.
Biodentine ; MM-MTA ; Push-outtest ; Root-end filling materials ; Total Fill RRM
Department of Biomedical, Surgical, and Dental Sciences, Galeazzi Institute, University of Milan, Milan, Italy
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o izdanju
22 (3)
2018.
1559-1565
objavljeno
1432-6981
1436-3771
10.1007/s00784-017-2244-6
Povezanost rada
Dentalna medicina, Kliničke medicinske znanosti