Autori: Rešković, Stoja; Vodopivec, Franc; Mamuzić, Ilija
Naslov: Nucleation and growth of Precipitaties of Niobium Carbonitride in the Final High-Temperature Thermomechanical Treatment
( Nucleation and growth of Precipitaties of Niobium Carbonitride in the Final High-Temperature Thermomechanical Treatment )
Izvornik: Sažeci predavanja s 3. Međunarodnog simpozija hrvatskih metalurga "Stanje i razvitak plastične obradbe kovina i slitina" tiskano u časopisu "Metalurgija" 37(1998)2, 103-132 / Mamuzić, Ilija (ur.). - Zagreb : Hrvatsko metalurško društvo , 1998. 118-118.
Skup: 3. Međunarodni simpozij hrvatskih metalurga
Mjesto i datum: Šibenik, Hrvatska, 25-27.06.1998.
Ključne riječi: nucleation; niobium carbonitride; high-temperature thermomechanical treatment
( nucleation; niobium carbonitride; high-temperature thermomechanical treatment )
Sažetak:
The paper deals with the results of niobium solving and precipitating in the course of thermomechanical treatment of microalloyed steel. Electrolytic isolation, X-ray phase analysis and transmission electron microscopy were applied to determinate the change of niobium precipitation degree, type and share of precipitates, as well as nucleation and the growth of precipitates across the phase of the final thermomechanical treatment. The degree of precipitation of niobium carbonitrides initiates a strong increase of induced precipitation. The nucleation of these precipitates occurs at dislocations inside the grain. Niobium carbides and niobium nitrides were identified.
Vrsta sudjelovanja: Poster
Vrsta prezentacije u zborniku: Sažetak
Vrsta recenzije: Međunarodna recenzija
Projekt / tema: 124002
Izvorni jezik: eng
Kategorija: Znanstveni
Znanstvena područja:
Metalurgija



  Verzija za printanje   za tiskati


upomoc
foot_4