Creep Fatigue Behaviour of Directionally Solidified Nickel Base Superalloy (CROSBI ID 80712)

Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija

Zrnik, Josef ; Yu, Y. ; Wang, J. A. ; Žitnansky, Marcel ; Mamuzić, Ilija ; Hornak, P. Creep Fatigue Behaviour of Directionally Solidified Nickel Base Superalloy // Metalurgija, 35 (1996), 1; 11-15

Podaci o odgovornosti

Zrnik, Josef ; Yu, Y. ; Wang, J. A. ; Žitnansky, Marcel ; Mamuzić, Ilija ; Hornak, P.

engleski

Creep Fatigue Behaviour of Directionally Solidified Nickel Base Superalloy

The static and cyclic creep load controlled tests of as-cast and heat treated single crystal nickel based superalloy CMSX 3 have been studied. Two different testing procedures were adopted. One is cyclic creep test with different hold times at maximum stress amplitude, and the other cyclic creep procedure is in which the mean stress was held constant at 400MPa. Different cycling frequency and amplitude ratios were superimposed on the mena stress. All the tests were carried out at 900C. The influence of those variables was evaluated through the deformation mechanism investigation and the life to fracture data.

creep fatigue behaviour ; nickel base superalloy ; deformation mechanism investigation

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

Podaci o izdanju

35 (1)

1996.

11-15

objavljeno

0543-5846

1334-2576

Povezanost rada

Metalurgija

Indeksiranost