Autori: Bukhanovskii, V. V.; Kharchenko, V. K.; Mamuzić, Ilija
Naslov: The Influence of Heat-Resistant Coatings on High-Temperature Strength of Niobium-Based Alloys (Nb-Mo-Zr-C)
( The Influence of Heat-Resistant Coatings on High-Temperature Strength of Niobium-Based Alloys (Nb-Mo-Zr-C) )
Izvornik: Sažeci predavanja s 7. međunarodnog simpozija Hrvatskog metalurškog društva "Materijali i metalurgija", tiskano u Metalurgija 45(2006)3, 195-219 / Mamuzić, Ilija (ur.). - Zagreb : Hrvatsko metalurško društvo , 2006. 204-204.
Skup: 7. međunarodni simpozij Hrvatskog metalurškog društva "Materijali i metalurgija"
Mjesto i datum: Šibenik, Hrvatska, 18-22. 06. 2006.
Ključne riječi: niobium-based alloy ; heat-resistant coatings ; high-temperature strength
( niobium-based alloy ; heat-resistant coatings ; high-temperature strength )
Sažetak:
This paper examines the strength, deformability, and load-carrying capacity of niobium-based alloys VN-3 and VN-9 (Nb-Mo-Zr-C), both in the initial state and with ceramic slip coatings based on molybdenum-hafnium silicides, under conditions of short- and long-term static tension in vacuum, inert medium, and in air in the temperature range from 1770 to 2020 K. A method has been developed to assess the damage accumulated in the niobium alloy/silicide-ceramic coating composite under high-temperature loading. As a result of studying the creep and long-term strength of the niobium alloy/silicide-ceramic coating composite, the values of 0, 5 % and 1, 0 % creep limits of the composites for test times of 0, 1 ; 1, 0 ; and 10 hours at temperatures of 1770 and 2020 K have been obtained.
Vrsta sudjelovanja: Poster
Vrsta prezentacije u zborniku: Sažetak
Vrsta recenzije: Međunarodna recenzija
Projekt / tema: 0124001
Izvorni jezik: eng
Kategorija: Znanstveni
Znanstvena područja:
Metalurgija



Verzija za printanje   za tiskati


upomoc
foot_4