Autori: Bukhanovskii, V. V.; Borisenko, V. A.; Kharchenko, V. K.; Mamuzić, Ilija
Naslov: High-Temperature Strength of Niobium Alloy 5VMTs with a Silicide-Ceramic Coating. Part 1. Short-Term Strength Characteristics
( High-Temperature Strength of Niobium Alloy 5VMTs with a Silicide-Ceramic Coating. Part 1. Short-Term Strength Characteristics )
Izvornik: Sažeci predavanja s 7. međunarodnog simpozija Hrvatskog metalurškog društva "Materijali i metalurgija", tiskano u Metalurgija 45(2006)3, 195-219 / Mamuzić, Ilija (ur.). - Zagreb : Hrvatsko metalurško društvo , 2006. 206-206.
Skup: 7. međunarodni simpozij Hrvatskog metalurškog društva "Materijali i metalurgija"
Mjesto i datum: Šibenik, Hrvatska, 18-22. 06. 2006.
Ključne riječi: niobium alloy ; silicide-ceramics coating ; high-temperature strength
( niobium alloy ; silicide-ceramics coating ; high-temperature strength )
Sažetak:
Experimental data on the short-term strength and plasticity of niobium alloy 5VMTs of the system Nb-W-Mo-Zr in its initial state, after annealing, and with a silicide-ceramic protective coating obtained by testing in vacuum, an inert atmosphere, and in air in the temperature range from 290 to 2270 K are analyzed. The process of microcrack initiation and propagation in the protective coating and matrix is investigated in high-temperature static tension. The limiting plastic strain values have been established at which the composite retains its load-carrying capacity in high-temperature aggressive and oxidizing gas atmospheres.
Vrsta sudjelovanja: Poster
Vrsta prezentacije u zborniku: Sažetak
Vrsta recenzije: Međunarodna recenzija
Projekt / tema: 0124001
Izvorni jezik: eng
Kategorija: Znanstveni
Znanstvena područja:
Metalurgija



Verzija za printanje   za tiskati


upomoc
foot_4