Evolution of substructure during continuous rolling of microalloyed steel strip (CROSBI ID 85597)

Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija

Vodopivec, Franc ; Rešković, Stoja ; Mamuzić, Ilija Evolution of substructure during continuous rolling of microalloyed steel strip // Materials science and technology, 15 (1999), 11; 1293-1299

Podaci o odgovornosti

Vodopivec, Franc ; Rešković, Stoja ; Mamuzić, Ilija

engleski

Evolution of substructure during continuous rolling of microalloyed steel strip

With the aim of investigating the evolution of the substructure, the rolling of a steel strip containing 0.13%C, 0.75%Mn, and 0.048%Nb (all wt-%) was interrupted and the partially rolled strip water quenched. Using X-ray diffraction spectra, subgrain size and dislocation density were determined for specimens taken before and after the rolling passes. Both these microstructural characteristics were related to the rolling temperature and the amount of NbC precipitation. The distribution of precipitates was investigated via TEM. At lower rolling temperature, particles precipitated in rows in the austenite temperature range.

microalloyed steel strip ; continuopus rolling ; substructure

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

Podaci o izdanju

15 (11)

1999.

1293-1299

objavljeno

0267-0836

Povezanost rada

Metalurgija

Indeksiranost