Autori: Reškovič, Stoja; Vodopivec, Franc; Novosel-Radović, Vjera; Mamuzić, Ilija
Naslov: The Influence of a Hot Plastic Deformation on the Crystal Latice Distortion Change of a Thermomechanical Treatment Microalloyed Steel
( The Influence of a Hot Plastic Deformation on the Crystal Latice Distortion Change of a Thermomechanical Treatment Microalloyed Steel )
Izvornik: Knjiga sažetaka - 5. međunarodno znanstveno savjetovanje proizvodnog strojarstva (CIM 99) / Cebalo, R. (ur.). - Zagreb : Croatian Assotiation of Production Engineering , 1999. 121-129.
Skup: 5. međunarodno znanstveno savjetovanje proizvodnog strojarstva
Mjesto i datum: Opatija, Hrvatska, 17-18. 06. 1999.
Ključne riječi: microalloyed steel; thermomechanical treatment; x-ray diffraction; crystal lattice distortion; precipitation; deformation; recrystalization
( microalloyed steel; thermomechanical treatment; x-ray diffraction; crystal lattice distortion; precipitation; deformation; recrystalization )
Sažetak:
The crystal lattice distortion change has been investigated in niobium microalloyed steel with 0.048% Nb. The final deformation of the thermomechanical treatment was performed on the fully continous rolling millin temperature range 987-887 C. X-ray diffraction was used for the examination of processes in substructure occurring during the rolling. The analysis of diffraction lines profile according to Warren and Averbach provided quantitative information on the crystal lattice distortion changes
Vrsta sudjelovanja: Predavanje
Vrsta prezentacije u zborniku: Cjeloviti rad (više od 1500 riječi)
Vrsta recenzije: Domaća recenzija
Projekt / tema: 124003
Izvorni jezik: eng
Kategorija: Znanstveni
Znanstvena područja:
Metalurgija



  Verzija za printanje   za tiskati


upomoc
foot_4