Influence of heat treatment on properties of ti-nb alloys (CROSBI ID 197590)
Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Kunčicka, L. ; Štěpan, P. ; Kliber, J. ; Mamuzić, Ilija
engleski
Influence of heat treatment on properties of ti-nb alloys
Ti-Nb alloys are of a large potential for industrial, as well as biomedical utilisation. Oxygen content in the alloy is a parameter influencing its properties and cannot be neglected. The main focus of this paper is on observation of influence of annealing time on oxygen content in the structure of Ti – 20, 7 (at.)% Nb alloy. Four groups of the samples were annealed at the temperature of 800 °C from 15 to 60 minutes with 15 min. step. As it was proven by the analysis, the oxygen content increased with increasing annealing time. Moreover, microhardness measurements showed increasing trend of HV microhardness value with increasing oxygen content.
titanium; oxygen content; microhardness
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano